Eye-and-Eye Slings High Performance slings – up to mbl 749 ton

Slings made from High Modulus Polyethylene (HMPE) have set new standards for lifting gear.
The Acera™ slings are made from Acera™ Amundsen 12 strand ropes.

Acera™ Amundsen are high performance ropes made from genuine Acera™ HMPE yarns, which are individually coated through a rotating 360° Kiss-roller process.
Single yarn coating is proven to significantly enhance internal and external abrasion resistance, and extend service life and strength. The sling eyes have Protech™ cover. A proprietary braided protection made from Acera™ yarn.  The splices are protected by a weaved polyester Y-cover.
All Acera™ slings are produced in accordance with own technical file based on ISO 18264:2016 standard. The eyes are hand-spliced with our own positive locking tuck variant, ensuring anti-slip under all circumstances. Acera™ slings are the alternative to cumbersome steel wires. They are stronger and safer. The corresponding weight is more than 7 times lower. Compared to conventional fiber ropes, the resulting reduction in diameter leads to significant savings in weight (60%), space and handling. Acera™ slings provide a safer and more productive lifting operation. The light weight, ultra strong Acera™ slings are available at a market competitive price and can be customised to suit numerous applications.

Suitable for:
Lifting Mooring Offshore Towing

Key Benefits

  • Less risk to the crew
  • Less injuries
  • 1/7 of weight steel wire ropes.
  • Easier handling
  • Faster operation
  • Less personnel needed
  • Higher lifting capacity
  • Less back injuries
  • No contact damage
  • No fraying or sharp edges
  • Superior bending flex fatigue
  • Easy to inspect and repair

Product Features

Construction
12-strand plaited core
Fiber
Acera™ HMPE
Specific gravity
HMPE cover 0,97 (floating)
Colours
Platinum
UV resistance
Excellent
Abbrasion resistance
Excellent
Acid resistance
Excellent
Alkali resitance
Excellent
Most chemicals resistance
Excellent
Cold & frost resistance
Excellent
Water resistance
Excellent (0% absorption)
Heat resistance
Low (145-150 melting)
Elongation
Low (2-3% at break)
Oil content in fiber
>0,1%
Cold & frost resistance
Excellent
Chemical resistance
Excellent
diameter MBL spliced MBL spliced Work Load Limit (WLL) Work Load Limit (WLL)
vertical and choker hitches SAFETY FACTOR 7:1
vertical and choker hitches SAFETY FACTOR 7:1
(mm) (t) (kN) (vertical t) (vertical kN)
6 3.37 33 0.48 4.71
8 6.02 59 0.86 8.39
10 9.38 92 1.34 13.14
12 13.5 132 1.92 18.86
14 18.4 180 2.62 25.71
16 24 235 3.42 33.57
18 28.9 283 4.12 40.43
20 34.7 340 4.95 48.57
22 40.8 400 5.83 57.14
24 47.9 470 6.85 67.14
26 55.1 540 7.87 77.14
28 62.2 610 8.89 87.14
30 70.4 690 10.05 98.57
32 79.5 780 11.36 111.43
34 87.7 860 12.53 122.86
36 95.9 940 13.69 134.29
38 106.1 1040 15.15 148.57
40 115.2 1130 16.46 161.43
44 133.6 1310 19.08 187.14
48 156 1530 22.29 218.57
52 180.5 1770 25.78 252.86
56 207 2030 29.57 290
60 232.5 2280 33.21 325.71
64 261 2560 37.29 365.71
68 290.6 2850 41.52 407.14
72 323.3 3170 46.18 452.86
76 356.9 3500 50.99 500
80 394.6 3870 56.38 552.86
84 435.8 4274 62.26 610.57
88 477.2 4680 68.18 668.57
92 516.7 5067 73.81 723.86
96 567 5560 81 794.29
100 604.4 5927 86.34 846.71
102 627.3 6152 89.62 878.86
104 650.8 6382 92.97 911.71
108 698.9 6854 99.84 979.14
112 748.7 7342 106.95 1048.86

Nominal diameter as per definition in ISO 1968. Minimum strength defined as MBF/ MBL (Minimum Breaking Force, minimum breakload) of spliced application, and measured in kilogram force/kp, tested according to ISO 2307 and verified by DNV GL. Work Load Limits ( WLL ) is measured in metric tons and kilonewtons based on a safety factor 7:1, as defined by the Machinery Directive 2006/42/EC.

Download Datasheet

Customer service

We have the local knowledge and industry expertise to find the best solution to cater for your needs, do not hesitate to get in touch and ask for an advice.